caa a22 4500 388021853 CHVBK 20180307124926.0 cr unu---uuuuu 161130e199807 xx s 000 0 eng 10.1557/JMR.1998.0245 doi S0884291400044812 pii (NATIONALLICENCE)cambridge-10.1557/JMR.1998.0245 Formation of cubic C-BN by crystallization of nano-amorphous solid at atmosphere [Elektronische Daten] An amorphous carbon-boron nitride (C-BN) solid was prepared by ball milling the mixture of graphite and hexagonal BN powders for a period of 120 h. After annealing the amorphous C-BN solid for 1 h at atmosphere in the temperature range from 800 to 900 K and then quenching it to room temperature, a small amount of cubic C-BN solid solutions with diamond-like structure, which belong to a high energy phase and can only be synthesized previously under high pressure and temperature (30 GPa, 2000 K), were observed in the annealed amorphous C-BN solid. The lattice constant of the cubic C-BN solid solution was 0.3587 nm, and its grain size was in the range of 10 to 50 nm. Copyright © Materials Research Society 1998 Yao Bin Department of Physics, Jilin University, Changchun 130023, People's Republic of China and State Key Lab of RSA, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, People's Republic of China Liu L. Department of Physics, Jilin University, Changchun 130023, People's Republic of China Su W. H. Department of Physics, Jilin University, Changchun 130023, People's Republic of China and International Centre for Materials Physics, Chinese Academy of Sciences, Shenyang 110015, People's Republic of China Journal of Materials Research Cambridge University Press 13/7(1998-07), 1753-1756 0884-2914 13:7<1753 1998 13 JMR https://doi.org/10.1557/JMR.1998.0245 text/html Onlinezugriff via DOI 1 research-article jats NATIONALLICENCE 856 40 https://doi.org/10.1557/JMR.1998.0245 text/html Onlinezugriff via DOI NATIONALLICENCE 700 1- Yao Bin Department of Physics, Jilin University, Changchun 130023, People's Republic of China and State Key Lab of RSA, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, People's Republic of China NATIONALLICENCE 700 1- Liu L. Department of Physics, Jilin University, Changchun 130023, People's Republic of China NATIONALLICENCE 700 1- Su W. H. Department of Physics, Jilin University, Changchun 130023, People's Republic of China and International Centre for Materials Physics, Chinese Academy of Sciences, Shenyang 110015, People's Republic of China NATIONALLICENCE 773 0- Journal of Materials Research Cambridge University Press 13/7(1998-07), 1753-1756 0884-2914 13:7<1753 1998 13 JMR CC0 http://creativecommons.org/publicdomain/zero/1.0 nationallicence BK010053 XK010053 XK010000 NATIONALLICENCE NATIONALLICENCE NL-cambridge