caa a22 4500 445860219 CHVBK 20180317145440.0 cr unu---uuuuu 170323e20110901xx s 000 0 eng 10.1007/s11041-011-9377-z doi (NATIONALLICENCE)springer-10.1007/s11041-011-9377-z Yazici A. Celal Bayar University, Turgutlu Vocational High School, Department of Machinery, 45400, Turgutlu-Manisa, Turkey aut Wear behavior of carbonitride-treated ploughshares produced from 30MnB5 steel for soil tillage applications [Elektronische Daten] [A. Yazici] The effects of gaseous carbonitriding processes on wear characteristics of 30MnB5 steel were investigated. The matrix of the carbonitride treated samples has a better wear resistance compared to the substrates of the conventionally heat-treated sample in laboratory conditions. The carbonitriding treatment condition giving rise to the lowest wear weight loss with the pin-on-disc wear machine was selected in order to harden ploughshare specimens to be tested in field experiments. The carbonitriding process at 860°C, with 0.9% C, and 0.6m3/h NH3 for 105min and quenched in 60°C oil followed by a 60min tempering process at 140°C decreased 14.65% of total wear weight loss and 26.47% of total wear dimension loss of the ploughshare specimens in comparison to the conventional heat treatment process in field operational conditions. Springer Science+Business Media, Inc., 2011 abrasion nationallicence hardfacing nationallicence steel nationallicence wear testing nationallicence soil tillage nationallicence Metal Science and Heat Treatment Springer US; http://www.springer-ny.com 53/5-6(2011-09-01), 248-253 0026-0673 53:5-6<248 2011 53 11041 https://doi.org/10.1007/s11041-011-9377-z text/html Onlinezugriff via DOI 1 research-article jats NATIONALLICENCE 856 40 https://doi.org/10.1007/s11041-011-9377-z text/html Onlinezugriff via DOI NATIONALLICENCE 100 1- Yazici A. Celal Bayar University, Turgutlu Vocational High School, Department of Machinery, 45400, Turgutlu-Manisa, Turkey aut NATIONALLICENCE 773 0- Metal Science and Heat Treatment Springer US; http://www.springer-ny.com 53/5-6(2011-09-01), 248-253 0026-0673 53:5-6<248 2011 53 11041 Metadata rights reserved Springer special CC-BY-NC licence nationallicence BK010053 XK010053 XK010000 NATIONALLICENCE NATIONALLICENCE NL-springer