caa a22 4500 463222490 CHVBK 20180405153216.0 cr unu---uuuuu 170326e20071001xx s 000 0 eng 10.1007/s10853-007-1700-0 doi (NATIONALLICENCE)springer-10.1007/s10853-007-1700-0 Growth rate of Nb3Sn for reactive diffusion between Nb and Cu-9.3Sn-0.3Ti alloy [Elektronische Daten] [Ken-ichiro Mikami, Masanori Kajihara] In order to examine experimentally the growth behavior of Nb3Sn during reactive diffusion between Nb and a bronze with the α+β two-phase microstructure, a sandwich (Cu-Sn-Ti)/Nb/(Cu-Sn-Ti) diffusion couple was prepared from pure Nb and a ternary Cu-Sn-Ti alloy with concentrations of 9.3 at.% Sn and 0.3 at.% Ti by a diffusion bonding technique. Here, α is the primary solid-solution phase of Cu with the face-centered cubic structure, and β is the intermediate phase with the body-centered cubic structure. The diffusion couple was isothermally annealed at temperatures between T=923 and 1,053K for various times up to 843h. Owing to annealing, the Nb3Sn layer is formed along each (Cu-Sn-Ti)/Nb interface in the diffusion couple, and grows mainly into Nb. Hence, the migration of the Nb3Sn/Nb interface governs the growth of the Nb3Sn layer. The mean thickness of the Nb3Sn layer is proportional to a power function of the annealing time. The exponent of the power function is close to unity at T=923K, but takes values of 0.8-0.7 at T=973-1,053K. Consequently, the interface reaction at the migrating Nb3Sn/Nb interface is the rate-controlling process for the growth of the Nb3Sn layer at T=923K, and the interdiffusion across the Nb3Sn layer as well as the interface reaction contributes to the rate-controlling process at T=973-1,053K. Except the effect of Ti, the growth rate of the Nb3Sn layer is predominantly determined by the activity of Sn in the bronze and thus the concentration of Sn in the α phase. As a result, the growth rate is hardly affected by the volume fraction of the β phase, though the final amount of the Nb3Sn layer may depend on the volume fraction. Springer Science+Business Media, LLC, 2007 Mikami Ken-ichiro Graduate School, Tokyo Institute of Technology, 226-8502, Yokohama, Japan aut Kajihara Masanori Department of Materials Science and Engineering, Tokyo Institute of Technology, 226-8502, Yokohama, Japan aut Journal of Materials Science Kluwer Academic Publishers-Plenum Publishers; http://www.springer-ny.com 42/19(2007-10-01), 8178-8188 0022-2461 42:19<8178 2007 42 10853 https://doi.org/10.1007/s10853-007-1700-0 text/html Onlinezugriff via DOI 1 research-article jats NATIONALLICENCE 856 40 https://doi.org/10.1007/s10853-007-1700-0 text/html Onlinezugriff via DOI NATIONALLICENCE 700 1- Mikami Ken-ichiro Graduate School, Tokyo Institute of Technology, 226-8502, Yokohama, Japan aut NATIONALLICENCE 700 1- Kajihara Masanori Department of Materials Science and Engineering, Tokyo Institute of Technology, 226-8502, Yokohama, Japan aut NATIONALLICENCE 773 0- Journal of Materials Science Kluwer Academic Publishers-Plenum Publishers; http://www.springer-ny.com 42/19(2007-10-01), 8178-8188 0022-2461 42:19<8178 2007 42 10853 Metadata rights reserved Springer special CC-BY-NC licence nationallicence BK010053 XK010053 XK010000 NATIONALLICENCE NATIONALLICENCE NL-springer