caa a22 4500 463231740 CHVBK 20180405153244.0 cr unu---uuuuu 170326e20071201xx s 000 0 eng 10.1007/s10853-007-1978-y doi (NATIONALLICENCE)springer-10.1007/s10853-007-1978-y Reaction of 316L stainless steel with a galvanizing bath [Elektronische Daten] [Ke Zhang, Nai-Yong Tang, Frank Goodwin, Scott Sexton] Type 316L stainless steel (316L SS), commonly used as pot roll material, was tested in an industrial Zn-Al galvanizing bath, with an effective Al content of 0.2wt.%. Samples welded to the supporting roll arms and sides of the sink roll experienced heavy dross buildup. Samples placed at locations away from the incoming strip generally experienced much less dross buildup. Dross particles within the buildup on samples attached to supporting roll arms were small in size but numerous while particles on samples welded to the sides of the sink roll were much larger. SEM-EDS analyses indicated that the buildup consisted of two layers. The inner layer was the product of the corrosive reaction of 316L SS with the bath metal, and the outer layer was formed by dross particles built up on the inner reaction layer. The intermetallic phase, which formed at the reaction front of the samples was the inhibition compound Fe2Al5 containing some Mo and Cr. The formation of this intermetallic layer provided a thermodynamically favourable base for the attachment and further buildup of suspended dross particles on the sample surfaces. Springer Science+Business Media, LLC, 2007 Zhang Ke Teck Cominco Metals Ltd, Product Technology Centre, 2380, Speakman Drive, L5K 1B4, Mississauga, ON, Canada aut Tang Nai-Yong Teck Cominco Metals Ltd, Product Technology Centre, 2380, Speakman Drive, L5K 1B4, Mississauga, ON, Canada aut Goodwin Frank International Lead Zinc Research Organization, Inc, 2525 Meridian Parkway, Suite 100, 27713, Durham, NC, USA aut Sexton Scott Nucor Steel - Crawfordsville Division, 4537 S. Nucor Road, 47933, Crawfordsville, IN, USA aut Journal of Materials Science Springer US; http://www.springer-ny.com 42/23(2007-12-01), 9736-9745 0022-2461 42:23<9736 2007 42 10853 https://doi.org/10.1007/s10853-007-1978-y text/html Onlinezugriff via DOI 1 research-article jats NATIONALLICENCE 856 40 https://doi.org/10.1007/s10853-007-1978-y text/html Onlinezugriff via DOI NATIONALLICENCE 700 1- Zhang Ke Teck Cominco Metals Ltd, Product Technology Centre, 2380, Speakman Drive, L5K 1B4, Mississauga, ON, Canada aut NATIONALLICENCE 700 1- Tang Nai-Yong Teck Cominco Metals Ltd, Product Technology Centre, 2380, Speakman Drive, L5K 1B4, Mississauga, ON, Canada aut NATIONALLICENCE 700 1- Goodwin Frank International Lead Zinc Research Organization, Inc, 2525 Meridian Parkway, Suite 100, 27713, Durham, NC, USA aut NATIONALLICENCE 700 1- Sexton Scott Nucor Steel - Crawfordsville Division, 4537 S. Nucor Road, 47933, Crawfordsville, IN, USA aut NATIONALLICENCE 773 0- Journal of Materials Science Springer US; http://www.springer-ny.com 42/23(2007-12-01), 9736-9745 0022-2461 42:23<9736 2007 42 10853 Metadata rights reserved Springer special CC-BY-NC licence nationallicence BK010053 XK010053 XK010000 NATIONALLICENCE NATIONALLICENCE NL-springer