caa a22 4500 46323409X CHVBK 20180405153251.0 cr unu---uuuuu 170326e20070801xx s 000 0 eng 10.1007/s10853-006-1157-6 doi (NATIONALLICENCE)springer-10.1007/s10853-006-1157-6 Thermal effects on fracture of biaxial-oriented poly(ethylene terephthalate) (BOPET) film [Elektronische Daten] [S. Hashemi, Y. Xu] The effect of temperature on the fracture behaviour of biaxial-oriented poly(ethylene terephthalate) (BOPET) film was studied using the Essential Work of Fracture (EWF) approach. Fracture tests were performed over the temperature range +25 to +160°C at the speed of 5mm/min using double edge notched tension (DENT) specimens. The length of the specimens was either along the machine direction (MD) (0°), transverse direction (TD) (90°) or at 45° to either MD or TD. Ductile tearing of the ligament region was noted over the entire temperature range in all three directions. A linear relationship was found between the specific total work of fracture and the ligament length at all test temperatures. Values of the specific essential work of fracture (w e) in the MD and TD were similar and smaller than in the 45° direction. Within temperature range 25-140°C, w e showed little variation if any with respect to temperature. As expected, the Specific Non-Essential Work of Fracture (βw p) was temperature dependent. This parameter increased with increasing temperature and reached a maximum around the glass transition temperature of BOPET (T g≈80°C). The values of the maxima are respectively 16.15, 20.38 and 17.8MJm−3 for the 0°, 45° and 90°. Springer Science+Business Media, LLC, 2007 Hashemi S. London Metropolitan Polymer Centre, London Metropolitan University, N7 8DB, London, UK aut Xu Y. London Metropolitan Polymer Centre, London Metropolitan University, N7 8DB, London, UK aut Journal of Materials Science Kluwer Academic Publishers-Plenum Publishers; http://www.springer-ny.com 42/15(2007-08-01), 6197-6204 0022-2461 42:15<6197 2007 42 10853 https://doi.org/10.1007/s10853-006-1157-6 text/html Onlinezugriff via DOI 1 research-article jats NATIONALLICENCE 856 40 https://doi.org/10.1007/s10853-006-1157-6 text/html Onlinezugriff via DOI NATIONALLICENCE 700 1- Hashemi S. London Metropolitan Polymer Centre, London Metropolitan University, N7 8DB, London, UK aut NATIONALLICENCE 700 1- Xu Y. London Metropolitan Polymer Centre, London Metropolitan University, N7 8DB, London, UK aut NATIONALLICENCE 773 0- Journal of Materials Science Kluwer Academic Publishers-Plenum Publishers; http://www.springer-ny.com 42/15(2007-08-01), 6197-6204 0022-2461 42:15<6197 2007 42 10853 Metadata rights reserved Springer special CC-BY-NC licence nationallicence BK010053 XK010053 XK010000 NATIONALLICENCE NATIONALLICENCE NL-springer