caa a22 4500 477122132 CHVBK 20180405111639.0 cr unu---uuuuu 170330e19960601xx s 000 0 eng 10.1007/BF03026090 doi (NATIONALLICENCE)springer-10.1007/BF03026090 Park No Department of Materials Science and Engineering, Kumoh National University of Technology, 730-701, Kumi, Korea aut Texture in CuZnAl shape memory alloys [Elektronische Daten] [No Park] The pseudoelastic elongation and the Young's modulus were estimated using lexture and orientation dependent properties in the 95.5% hot-rolled Cu-14.0 wt% Zn-8.0 wt% Al, in the 96.7% extruded Cu -17.7 wt% Zn-7.0 wt% Al-0.5 wt%Ti and in the 95% cold drawn Cu-27.1 wt% Zn-4.6 wt% Al shape-memory-alloys. The textures were measured in martensitic phases, and the austenitic textures were calculated using texture transformation, which gave rise to the maximum possible shape change for a particular application. The maximum value of the pseudoelastic elongation (6.55%) was found at the normal direction in the sheet and a minimum value of 2.23% at 35° from the normal direction to the rolling direction. In the rod and wire the maximum value 4.80% and 5.28% were found at 45 and 90° from the axis direction. The anisotropic constant 1.5, 1.2 and 1.3 of the Young's modulus were found in the sheet, rod and wire, respectively. These values enabled us to estimate the optimum texture for a technological application. Springer, 1996 Metals and Materials The Korean Institute of Metals and Materials 2/3(1996-06-01), 159-168 1598-9623 2:3<159 1996 2 12540 https://doi.org/10.1007/BF03026090 text/html Onlinezugriff via DOI 1 research-article jats NATIONALLICENCE 856 40 https://doi.org/10.1007/BF03026090 text/html Onlinezugriff via DOI NATIONALLICENCE 100 1- Park No Department of Materials Science and Engineering, Kumoh National University of Technology, 730-701, Kumi, Korea aut NATIONALLICENCE 773 0- Metals and Materials The Korean Institute of Metals and Materials 2/3(1996-06-01), 159-168 1598-9623 2:3<159 1996 2 12540 Metadata rights reserved Springer special CC-BY-NC licence nationallicence BK010053 XK010053 XK010000 NATIONALLICENCE NATIONALLICENCE NL-springer